LEXAN?
500 resin
聚碳酸酯
10%
玻璃纖維增強(qiáng)材料
產(chǎn)品說明:
10% GR PC. Optimum combination of high modulus plus excellent impact
strength and flame retardance.
|
材料狀態(tài)
|
|
|
資料 1
|
|
|
UL 黃卡 2
|
|
|
搜索 UL
黃卡
|
|
|
供貨地區(qū)
|
|
|
填料/增強(qiáng)材料
|
-
玻璃纖維增強(qiáng)材料, 10% 填料按重量
|
|
特性
|
|
|
加工方法
|
|
|
比重
|
|
|
ASTM
D792
|
|
--
|
1.27
|
g/cm?
|
|
|
--
|
1.25
|
g/cm?
|
|
|
特定體積
|
0.802
|
cm?/g
|
ASTM
D792
|
|
熔流率（熔體流動(dòng)速率） (300°C/1.2
kg)
|
7.5
|
g/10 min
|
ASTM
D1238
|
|
收縮率 - 流動(dòng) (3.20 mm)
|
0.20 到 0.40
|
%
|
內(nèi)部方法
|
|
吸水率
|
|
|
ASTM
D570
|
|
24
hr
|
0.12
|
%
|
|
|
平衡,
23°C
|
0.31
|
%
|
|
|
室外適用性
|
f2
|
|
UL
746C
|
|
洛氏硬度
|
|
|
ASTM
D785
|
|
M
級(jí)
|
85
|
|
|
|
R
級(jí)
|
124
|
|
|
|
抗張強(qiáng)度 3
|
|
|
ASTM
D638
|
|
屈服
|
66.2
|
MPa
|
|
|
斷裂
|
55.2
|
MPa
|
|
|
伸長(zhǎng)率 3
|
|
|
ASTM
D638
|
|
屈服
|
8.0
|
%
|
|
|
斷裂
|
15
|
%
|
|
|
彎曲模量 4 (50.0 mm 跨距)
|
3450
|
MPa
|
ASTM
D790
|
|
彎曲強(qiáng)度 4 (屈服, 50.0 mm
跨距)
|
103
|
MPa
|
ASTM
D790
|
|
泰伯耐磨性 (1000 Cycles, 1000 g, CS-17
轉(zhuǎn)輪)
|
11.0
|
mg
|
ASTM
D1044
|
|
懸壁梁缺口沖擊強(qiáng)度 (23°C)
|
110
|
J/m
|
ASTM
D256
|
|
無缺口懸臂梁沖擊 (23°C)
|
2100
|
J/m
|
ASTM
D4812
|
|
落錘沖擊 (23°C)
|
102
|
J
|
ASTM
D3029
|
|
拉伸沖擊強(qiáng)度 5
|
158
|
kJ/m?
|
ASTM
D1822
|
|
載荷下熱變形溫度
|
|
|
ASTM
D648
|
|
0.45 MPa,
未退火, 6.40 mm
|
146
|
°C
|
|
|
1.8 MPa,
未退火, 6.40 mm
|
142
|
°C
|
|
|
維卡軟化溫度
|
154
|
°C
|
ASTM
D1525 6
|
|
線形熱膨脹系數(shù) - 流動(dòng) (-40 到 95°C)
|
3.2E-5
|
cm/cm/°C
|
ASTM
E831
|
|
比熱
|
1210
|
J/kg/°C
|
ASTM
C351
|
|
導(dǎo)熱系數(shù)
|
0.20
|
W/m/K
|
ASTM
C177
|
|
RTI Elec
|
130
|
°C
|
UL
746
|
|
RTI Imp
|
130
|
°C
|
UL
746
|
|
RTI
|
130
|
°C
|
UL
746
|
|
體積電阻率
|
> 1.0E+17
|
ohm·cm
|
ASTM
D257
|
|
介電強(qiáng)度 (3.20 mm, in
Air)
|
18
|
kV/mm
|
ASTM
D149
|
|
介電常數(shù)
|
|
|
ASTM
D150
|
|
50
Hz
|
3.10
|
|
|
|
60
Hz
|
3.10
|
|
|
|
1
MHz
|
3.05
|
|
|
|
耗散因數(shù)
|
|
|
ASTM
D150
|
|
50
Hz
|
8.0E-4
|
|
|
|
60
Hz
|
8.0E-4
|
|
|
|
1
MHz
|
7.5E-3
|
|
|
|
耐電弧性 7
|
PLC 7
|
|
ASTM
D495
|
|
相比耐漏電起痕指數(shù)(CTI)
|
PLC 3
|
|
UL
746
|
|
高電弧燃燒指數(shù)(HAI)
|
PLC 4
|
|
UL
746
|
|
高電壓電弧起痕速率 (HVTR)
|
PLC 4
|
|
UL
746
|
|
熱絲引燃 (HWI)
|
PLC 1
|
|
UL
746
|
|
UL 阻燃等級(jí)
|
|
|
UL
94
|
|
1.52
mm
|
V-0
|
|
|
|
3.05
mm
|
5VA
|
|
|
|
極限氧指數(shù)
|
36
|
%
|
ASTM
D2863
|
|
Radiant Panel Listing
(UL)
|
YES
|
|
|
|
干燥溫度
|
121
|
°C
|
|
|
干燥時(shí)間
|
3.0 到 4.0
|
hr
|
|
|
干燥時(shí)間，最大
|
48
|
hr
|
|
|
建議的最大水分含量
|
0.020
|
%
|
|
|
建議注射量
|
40 到 60
|
%
|
|
|
料筒后部溫度
|
288 到 310
|
°C
|
|
|
料筒中部溫度
|
299 到 321
|
°C
|
|
|
料筒前部溫度
|
310 到 332
|
°C
|
|
|
射嘴溫度
|
304 到 327
|
°C
|
|
|
加工（熔體）溫度
|
310 到 332
|
°C
|
|
|
模具溫度
|
82.2 到 116
|
°C
|
|
|
背壓
|
0.345 到 0.689
|
MPa
|
|
|
螺桿轉(zhuǎn)速
|
40 到 70
|
rpm
|
|
|
排氣孔深度
|
0.025 到 0.076
|
mm
|
|
|
在線咨詢 