Bayblend®
FR3050
聚碳酸酯+丙烯腈丁二烯苯乙烯
產(chǎn)品說明:
(PC+ABS) blend; unreinforced; flame-retardant; high heat resistant
injection molding grade; improved chemical resistance and stress cracking
behavior compared to KU2-1514; ball indentation temperature >= 125 °C;
Vicat/B 120 temperature = 136 °C; UL recognition 94 V-1 at 1.0 mm; suitable as
supporting material for energized parts.
|
材料狀態(tài)
|
|
|
資料 1
|
|
|
UL 黃卡 2
|
|
|
搜索 UL
黃卡
|
|
|
供貨地區(qū)
|
|
|
添加劑
|
|
|
特性
|
|
|
RoHS 合規(guī)性
|
|
|
加工方法
|
|
|
密度 (23°C)
|
1.19
|
g/cm?
|
ISO
1183
|
|
溶化體積流率（MVR） (260°C/5.0
kg)
|
18.0
|
cm?/10min
|
ISO
1133
|
|
收縮率 3
|
|
|
ISO
2577
|
|
垂直流動方向 :
260°C, 3.00 mm
|
0.50 到 0.70
|
%
|
|
|
流動方向 :
260°C, 3.00 mm
|
0.50 到 0.70
|
%
|
|
|
吸水率
|
|
|
ISO
62
|
|
飽和,
23°C
|
0.50
|
%
|
|
|
平衡, 23°C,
50% RH
|
0.20
|
%
|
|
|
拉伸模量 (23°C)
|
2400
|
MPa
|
ISO
527-2/1
|
|
拉伸應(yīng)力
|
|
|
ISO
527-2/50
|
|
屈服,
23°C
|
65.0
|
MPa
|
|
|
斷裂,
23°C
|
60.0
|
MPa
|
|
|
拉伸應(yīng)變
|
|
|
ISO
527-2/50
|
|
屈服,
23°C
|
5.0
|
%
|
|
|
斷裂,
23°C
|
> 50
|
%
|
|
|
懸壁梁缺口沖擊強度
|
|
|
ISO
180/A
|
|
-30°C
|
15
|
kJ/m?
|
|
|
23°C
|
55
|
kJ/m?
|
|
|
無缺口伊佐德沖擊強度 (23°C)
|
無斷裂
|
|
ISO
180
|
|
熱變形溫度
|
|
|
|
|
0.45 MPa,
未退火
|
126
|
°C
|
ISO
75-2/B
|
|
1.8 MPa,
未退火
|
115
|
°C
|
ISO
75-2/A
|
|
維卡軟化溫度
|
|
|
|
|
--
|
134
|
°C
|
ISO
306/B50
|
|
--
|
136
|
°C
|
ISO
306/B120
|
|
線形熱膨脹系數(shù)
|
|
|
ISO
11359-2
|
|
流動 : 23 到
55°C
|
6.8E-5
|
cm/cm/°C
|
|
|
橫向 : 23 到
55°C
|
6.8E-5
|
cm/cm/°C
|
|
|
表面電阻率
|
1.0E+17
|
ohm
|
IEC
60093
|
|
體積電阻率 (23°C)
|
1.0E+17
|
ohm·cm
|
IEC
60093
|
|
介電強度 (23°C, 1.00
mm)
|
35
|
kV/mm
|
IEC
60243-1
|
|
相對電容率
|
|
|
IEC
60250
|
|
23°C, 100
Hz
|
3.20
|
|
|
|
23°C, 1
MHz
|
3.10
|
|
|
|
耗散因數(shù)
|
|
|
IEC
60250
|
|
23°C, 100
Hz
|
2.0E-3
|
|
|
|
23°C, 1
MHz
|
8.0E-3
|
|
|
|
漏電起痕指數(shù) (解決方案 A)
|
300
|
V
|
IEC
60112
|
|
UL 阻燃等級
|
|
|
UL
94
|
|
1.00
mm
|
V-1
|
|
|
|
1.50
mm
|
V-0
|
|
|
|
2.00
mm
|
5VB
|
|
|
|
3.00
mm
|
5VA
|
|
|
|
熔體粘度 (260°C, 1000
sec^-1)
|
480
|
Pa·s
|
ISO
11443-A
|
|