可獲得超合金化焊縫金屬的酸性金紅石型藥皮焊條。適合將耐酸不銹鋼焊接到低碳鋼和低合金鋼上。也適用于在使用耐酸不銹鋼焊縫金屬堆焊低碳鋼時的過渡層焊接。
典型拉伸性能
|
As welded
|
|
保護氣體
|
屈服強度
|
延伸率
|
抗拉強度
|
|
ISO
|
510 MPa
|
32 %
|
610 MPa
|
|
AWS
|
-
|
-
|
-
|
夏比V型缺口沖擊性能
|
As welded
|
|
保護氣體
|
沖擊值
|
測試溫度
|
|
ISO
|
50 J
|
20 °C
|
|
ISO
|
35 J
|
-20 °C
|
焊縫金屬分析
|
Mn
|
Mo
|
C
|
Si
|
Ferrite FN
|
Ni
|
N
|
Cr
|
|
0.6 %
|
2.8 %
|
0.02 %
|
0.8 %
|
18 %
|
13.4 %
|
22.5 %
|
熔敷數(shù)據(jù)
|
Fusion time per electrode at 90% I max
|
kg weld metal/kg electrodes
|
Number of electrodes/kg weld metal
|
安培
|
熔敷率
|
電壓 V
|
直徑
|
|
48 sec
|
0.58 kg
|
147
|
40-60 A
|
0.6 kg/h
|
26 V
|
2.0 x 300 mm
|
|
45 sec
|
0.57 kg
|
94
|
50-90 A
|
0.9 kg/h
|
29 V
|
2.5 x 300 mm
|
|
61 sec
|
0.59 kg
|
47
|
60-120 A
|
1.4 kg/h
|
27 V
|
3.2 x 350 mm
|
|
56 sec
|
0.61 kg
|
32
|
85-180 A
|
2.0 kg/h
|
31 V
|
4.0 x 350 mm
|
|
64 sec
|
0.59 kg
|
20
|
110-250 A
|
2.7 kg/h
|
30 V
|
5.0 x 350 mm
|
|
認(rèn)證:
|
SS to C&C/Mn steels, ABS, 309Mo, BV, EN 13479, CE, CSA W48: E309LMo-17, CWB, 30.039.05, DB, VL 309 Mo, DNV-GL, SS/CMn, LR, 309Mo, RINA, UNA 272580, Seproz, 02424, VdT?V
|
|
分類:
|
E 23 12 2 L R 3 2, EN ISO 3581-A, E309LMo-17, SFA/AWS A5.4, E309LMo-17, CSA W48, 1.4459, Werkstoffnummer
|
認(rèn)證均基于工廠的所在地。如需更多信息，請聯(lián)系伊薩。
|
Coating Type:
|
Acid Rutile
|
|
Ferrite Content:
|
FN 12-22
|
|
Welding Current:
|
DC+, AC
|
|
合金類型:
|
Austenitic CrNi
|
|