POM FM090臺(tái)灣寶理:
|
密度 / 比重
|
1.41
|
g/cm?
|
ASTM D792
|
|
熔流率（熔體流動(dòng)速率） (190°C/2.16 kg)
|
9.0
|
g/10 min
|
ASTM D1238
|
|
收縮率 - 流動(dòng) (3.00 mm)
|
1.8 到 2.2
|
%
|
ASTM D955
|
|
吸水率 (平衡, 23°C, 69%RH)
|
0.22
|
%
|
ASTM D570
|
|
洛氏硬度
|
|
|
ASTM D785
|
|
M 級(jí)
|
80
|
|
|
|
R 級(jí)
|
115
|
|
|
|
抗張強(qiáng)度 (屈服)
|
60.8
|
MPa
|
ASTM D638
|
|
伸長(zhǎng)率 (斷裂)
|
60
|
%
|
ASTM D638
|
|
彎曲模量
|
2550
|
MPa
|
ASTM D790
|
|
彎曲強(qiáng)度
|
93.2
|
MPa
|
ASTM D790
|
|
壓縮強(qiáng)度
|
|
|
ASTM D695
|
|
1% 應(yīng)變
|
31.4
|
MPa
|
|
|
10% 應(yīng)變
|
108
|
MPa
|
|
|
懸壁梁缺口沖擊強(qiáng)度 (23°C)
|
64
|
J/m
|
ASTM D256
|
|
載荷下熱變形溫度
|
|
|
ASTM D648
|
|
0.45 MPa, 未退火
|
158
|
°C
|
|
|
1.8 MPa, 未退火
|
110
|
°C
|
|
|
維卡軟化溫度
|
162
|
°C
|
ASTM D1525
|
|
熔融溫度
|
165
|
°C
|
DSC
|
|
線(xiàn)形熱膨脹系數(shù) - 流動(dòng)
|
8.5E-5
|
cm/cm/°C
|
ASTM D696
|
|
表面電阻率 3
|
1.0E+16
|
ohms
|
ASTM D257
|
|
體積電阻率 3 (23°C)
|
1.0E+14
|
ohms·cm
|
ASTM D257
|
|
介電強(qiáng)度 (2.00 mm)
|
24
|
kV/mm
|
ASTM D149
|
|
介電常數(shù)
|
|
|
IEC 60250
|
|
50 Hz
|
3.80
|
|
|
|
1 kHz
|
3.80
|
|
|
|
1 MHz
|
3.80
|
|
|
|