TYPICAL PROPERTIES (1)
|
|
MECHANICAL/機械性能
|
Value/值
|
Unit/單位
|
Standard/標(biāo)準(zhǔn)
|
|
Tensile Stress, yld, Type I / 抗張程度,屈服,類型I, 50 mm/min
|
58
|
MPa
|
ASTM D 638
|
|
Tensile Stress, brk, Type I / 抗張程度,斷裂,類型I, 50 mm/min
|
58
|
MPa
|
ASTM D 638
|
|
Tensile Strain, yld, Type I / 拉伸伸長,屈服,類型I, 50 mm/min
|
20
|
%
|
ASTM D 638
|
|
Tensile Strain, brk, Type I / 拉伸伸長,斷裂,類型I, 50 mm/min
|
20
|
%
|
ASTM D 638
|
|
Tensile Modulus / 拉伸模量, 5 mm/min
|
2820
|
MPa
|
ASTM D 638
|
|
Flexural Stress, yld / 撓曲強度, 屈服 , 1.3 mm/min, 50 mm span
|
101
|
MPa
|
ASTM D 790
|
|
Flexural Modulus / 撓曲模量, 1.3 mm/min, 50 mm span
|
2620
|
MPa
|
ASTM D 790
|
|
Taber Abrasion / 泰伯磨耗量, CS-17, 1 kg
|
19
|
mg/1000cy
|
SABIC Method
|
|
Tensile Stress, yield / 抗張程度,屈服, 50 mm/min
|
55
|
MPa
|
ISO 527
|
|
Tensile Stress, break / 抗張程度,斷裂, 50 mm/min
|
40
|
MPa
|
ISO 527
|
|
Tensile Strain, yield / 拉伸伸長,屈服, 50 mm/min
|
6
|
%
|
ISO 527
|
|
Tensile Strain, break / 拉伸伸長,斷裂, 50 mm/min
|
20
|
%
|
ISO 527
|
|
Tensile Modulus / 拉伸模量, 1 mm/min
|
2800
|
MPa
|
ISO 527
|
|
Flexural Stress, yield / 彎曲強度,屈服, 2 mm/min
|
80
|
MPa
|
ISO 178
|
|
Flexural Modulus / 撓曲模量, 2 mm/min
|
2600
|
MPa
|
ISO 178
|
|
Hardness / 硬度, H358/30
|
105
|
MPa
|
ISO 2039-1
|
|
Hardness，Rockwell / 洛氏硬度 R
|
120
|
–
|
ISO 2039-2
|
|
IMPACT/沖擊性能
|
Value/值
|
Unit/單位
|
Standard/標(biāo)準(zhǔn)
|
|
Izod Impact, unnotched / 無缺口懸臂梁沖擊, 23°C
|
1602
|
J/m
|
ASTM D 4812
|
|
Izod Impact, notched / 懸臂梁缺口沖擊強度, 23°C
|
37
|
J/m
|
ASTM D 256
|
|
Izod Impact, notched / 懸臂梁缺口沖擊強度, -30°C
|
22
|
J/m
|
ASTM D 256
|
|
Instrumented IMPACT Total Energy / 裝有測量儀表的落鏢沖擊總能量, 23°C
|
200
|
J
|
ASTM D 3763
|
|
Izod Impact, unnotched / 無缺口懸臂梁沖擊 80*10*4 +23°C
|
NB
|
kJ/m2
|
ISO 180/1U
|
|
Izod Impact, unnotched / 無缺口懸臂梁沖擊 80*10*4 -30°C
|
NB
|
kJ/m2
|
ISO 180/1U
|
|
Izod Impact, notched / 懸臂梁缺口沖擊強度 80*10*4 +23°C
|
5
|
kJ/m2
|
ISO 180/1A
|
|
Izod Impact, notched / 懸臂梁缺口沖擊強度 80*10*4 -30°C
|
3
|
kJ/m2
|
ISO 180/1A
|
|
Charpy（簡支梁缺口沖擊強度） 23°C, V-notch（V型切口） Edgew 80*10*4 sp=62mm
|
8
|
kJ/m2
|
ISO 179/1eA
|
|
Charpy Impact, notched /簡支梁缺口沖擊強度, 23°C
|
4
|
kJ/m2
|
ISO 179/2C
|
|
Charpy（簡支梁缺口沖擊強度） -30°C, V-notch（V型切口） Edgew 80*10*4 sp=62mm
|
4
|
kJ/m2
|
ISO 179/1eA
|
|
Charpy（簡支梁缺口沖擊強度） 23°C, Unnotch（無缺口） Edgew 80*10*4 sp=62mm
|
NB
|
kJ/m2
|
ISO 179/1eU
|
|
Charpy（簡支梁缺口沖擊強度） -30°C, Unnotch（無缺口） Edgew 80*10*4 sp=62mm
|
NB
|
kJ/m2
|
ISO 179/1eU
|
|
THERMAL/熱性能
|
Value/值
|
Unit/單位
|
Standard/標(biāo)準(zhǔn)
|
|
Vicat Softening Temp, Rate / 維卡軟化溫度，等級 B/50
|
165
|
°C
|
ASTM D 1525
|
|
HDT（熱變形溫度）, 1.82 MPa, 3.2mm, unannealed （未退火）
|
74
|
°C
|
ASTM D 648
|
|
HDT（熱變形溫度）, 0.45 MPa, 6.4 mm, unannealed （未退火）
|
162
|
°C
|
ASTM D 648
|
|
HDT（熱變形溫度）, 1.82 MPa, 6.4 mm, unannealed （未退火）
|
71
|
°C
|
ASTM D 648
|
|
CTE（線形膨脹系數(shù)）, -40°C to 40°C, flow（流動）
|
7.92E-05
|
1/°C
|
ASTM E 831
|
|
CTE（線形膨脹系數(shù)）, -40°C to 40°C, xflow（橫向）
|
7.92E-05
|
1/°C
|
ASTM E 831
|
|
CTE（線形膨脹系數(shù)）, 60°C to 138°C, flow（流動）
|
1.31E-04
|
1/°C
|
ASTM E 831
|
|
Thermal Conductivity / 導(dǎo)熱系數(shù)
|
0.24
|
W/m-°C
|
ISO 8302
|
|
CTE（線形膨脹系數(shù)）, 23°C to 60°C, flow（流動）
|
1.E-04
|
1/°C
|
ISO 11359-2
|
|
CTE（線形膨脹系數(shù)）, 23°C to 60°C, xflow（橫向）
|
1.E-04
|
1/°C
|
ISO 11359-2
|
|
Ball Pressure Test, 125°C +/- 2°C
|
PASSES
|
–
|
IEC 60695-10-2
|
|
Vicat Softening Temp, Rate / 維卡軟化溫度，等級 A/50
|
212
|
°C
|
ISO 306
|
|
Vicat Softening Temp, Rate / 維卡軟化溫度，等級 B/50
|
165
|
°C
|
ISO 306
|
|
Vicat Softening Temp, Rate / 維卡軟化溫度，等級 B/120
|
165
|
°C
|
ISO 306
|
|
HDT（熱變形溫度）/Be, 0.45MPa Edgew 120*10*4 sp=100mm
|
135
|
°C
|
ISO 75/Be
|
|
HDT（熱變形溫度）/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm
|
60
|
°C
|
ISO 75/Ae
|
|
Relative Temp Index, Elec / 相對熱指數(shù)， 電性能
|
120
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/impact / 相對熱指數(shù)，機械沖擊性能
|
120
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/o impact / 相對熱指數(shù)，非機械沖擊性能
|
140
|
°C
|
UL 746B
|
|
PHYSICAL/物理性能
|
Value/值
|
Unit/單位
|
Standard/標(biāo)準(zhǔn)
|
|
Specific Gravity / 比重
|
1.4
|
–
|
ASTM D 792
|
|
Specific Volume / 比容
|
0.71
|
cm3/g
|
ASTM D 792
|
|
Mold Shrinkage on Tensile Bar / 收縮率, flow（流動） (2)
|
1.1 – 1.8
|
%
|
SABIC Method
|
|
Mold Shrinkage / 收縮率, flow（流動）, 3.2 mm
|
1.5 – 2.3
|
%
|
SABIC Method
|
|
Mold Shrinkage / 收縮率, flow（流動）, 0.75-2.3 mm
|
0.9 – 1.6
|
%
|
SABIC Method
|
|
Mold Shrinkage / 收縮率, flow（流動）, 2.3-4.6 mm
|
1.5 – 2.3
|
%
|
SABIC Method
|
|
Mold Shrinkage on Tensile Bar / 收縮率, xflow（橫向） (2)
|
0.9 – 1.9
|
%
|
SABIC Method
|
|
Mold Shrinkage / 收縮率, xflow（橫向）, 0.75-2.3 mm
|
1 – 1.7
|
%
|
SABIC Method
|
|
Mold Shrinkage / 收縮率, xflow（橫向）, 2.3-4.6 mm
|
1.6 – 2.4
|
%
|
SABIC Method
|
|
Melt Flow Rate / 熔流率,, 250°C/2.16 kgf
|
8.6
|
g/10 min
|
ASTM D 1238
|
|
Density / 密度
|
1.4
|
g/cm3
|
ISO 1183
|
|
Water Absorption / 吸水率, (23°C/sat)
|
0.36
|
%
|
ISO 62
|
|
Moisture Absorption / 吸水率, 平衡 (23°C / 50% RH)
|
0.08
|
%
|
ISO 62
|
|
Melt Volume Rate / 溶化體積流率, MVR at 250°C/2.16 kg
|
8
|
cm3/10 min
|
ISO 1133
|
|
ELECTRICAL/電氣性能
|
Value/值
|
Unit/單位
|
Standard/標(biāo)準(zhǔn)
|
|
Dielectric Strength, in air / 介電強度，空氣中, 3.2 mm
|
18.4
|
kV/mm
|
ASTM D 149
|
|
Dielectric Strength, in oil / 耐電強度，在油中, 1.6 mm
|
22
|
kV/mm
|
ASTM D 149
|
|
Arc Resistance, Tungsten / 耐電弧性 {PLC}
|
6
|
PLC Code
|
ASTM D 495
|
|
Hot Wire Ignition / 熱絲引燃 {PLC)
|
2
|
PLC Code
|
UL 746A
|
|
High Voltage Arc Track Rate / 高電壓電弧起痕速率 {PLC}
|
4
|
PLC Code
|
UL 746A
|
|
High Voltage Arc Resistance {PLC)
|
6
|
PLC Code
|
UL 746A
|
|
High Ampere Arc Ign, surface / 高電流電弧引燃，表面 {PLC}
|
0
|
PLC Code
|
UL 746A
|
|
Comparative Tracking Index / 相比耐漏電起痕指數(shù) (UL) {PLC}
|
3
|
PLC Code
|
UL 746A
|
|
Volume Resistivity / 體積電阻率
|
>1.E+15
|
Ohm-cm
|
IEC 60093
|
|
Surface Resistivity ROA / 表面電阻率
|
>1.E+15
|
Ohm
|
IEC 60093
|
|
Dielectric Strength, shorttime, 1.0mm
|
18
|
kV/mm
|
IEC 60243-1
|
|
Dielectric Strength, in oil / 耐電強度，在油中, 0.8 mm
|
31
|
kV/mm
|
IEC 60243-1
|
|
Dielectric Strength, in oil / 耐電強度，在油中, 1.6 mm
|
24
|
kV/mm
|
IEC 60243-1
|
|
Dielectric Strength, in oil / 耐電強度，在油中, 3.2 mm
|
15
|
kV/mm
|
IEC 60243-1
|
|
Relative Permittivity / 相對介電常數(shù), 50/60 Hz
|
2.9
|
–
|
IEC 60250
|
|
Relative Permittivity / 相對介電常數(shù), 100 Hz
|
3.1
|
–
|
IEC 60250
|
|
Relative Permittivity / 相對介電常數(shù), 1 MHz
|
2.8
|
–
|
IEC 60250
|
|
Dissipation Factor / 耗散因素, 50/60 Hz
|
0.001
|
–
|
IEC 60250
|
|
Dissipation Factor / 耗散因素, 100 Hz
|
0.002
|
–
|
IEC 60250
|
|
Dissipation Factor / 耗散因素, 1 MHz
|
0.01
|
–
|
IEC 60250
|
|
Comparative Tracking Index / 相比耐漏電起痕指數(shù)
|
175
|
V
|
IEC 60112
|
|
Comparative Tracking Index / 相比耐漏電起痕指數(shù), M
|
100
|
V
|
IEC 60112
|
|
FLAME CHARACTERISTICS/火焰特性
|
Value/值
|
Unit/單位
|
Standard/標(biāo)準(zhǔn)
|
|
UL Recognized, 94V-0 Flame Class Rating / 阻燃等級 (3)
|
0.71
|
mm
|
UL 94
|
|
UL Recognized, 94-5VA Rating (3)
|
3
|
mm
|
UL 94
|
|
Glow Wire Flammability Index / 灼熱絲易燃指數(shù) 960°C, passes at
|
1
|
mm
|
IEC 60695-2-12
|
|
Oxygen Index / 極限氧指數(shù) (LOI)
|
30
|
%
|
ISO 4589
|