TYPICAL PROPERTIES (1)
|
|
MECHANICAL/機(jī)械性能
|
Value/值
|
Unit/單位
|
Standard/標(biāo)準(zhǔn)
|
|
Tensile Stress, yld, Type I / 抗張程度,屈服,類型I, 50 mm/min
|
58
|
MPa
|
ASTM D 638
|
|
Tensile Stress, brk, Type I / 抗張程度,斷裂,類型I, 50 mm/min
|
61
|
MPa
|
ASTM D 638
|
|
Tensile Strain, yld, Type I / 拉伸伸長,屈服,類型I, 50 mm/min
|
6
|
%
|
ASTM D 638
|
|
Tensile Strain, brk, Type I / 拉伸伸長,斷裂,類型I, 50 mm/min
|
130
|
%
|
ASTM D 638
|
|
Tensile Modulus / 拉伸模量, 50 mm/min
|
2100
|
MPa
|
ASTM D 638
|
|
Flexural Stress, yld / 撓曲強(qiáng)度, 屈服 , 1.3 mm/min, 50 mm span
|
88
|
MPa
|
ASTM D 790
|
|
Flexural Modulus / 撓曲模量, 1.3 mm/min, 50 mm span
|
2060
|
MPa
|
ASTM D 790
|
|
Tensile Stress, yield / 抗張程度,屈服, 50 mm/min
|
55
|
MPa
|
ISO 527
|
|
Tensile Stress, break / 抗張程度,斷裂, 50 mm/min
|
60
|
MPa
|
ISO 527
|
|
Tensile Strain, yield / 拉伸伸長,屈服, 50 mm/min
|
6
|
%
|
ISO 527
|
|
Tensile Strain, break / 拉伸伸長,斷裂, 50 mm/min
|
125
|
%
|
ISO 527
|
|
Tensile Modulus / 拉伸模量, 1 mm/min
|
2100
|
MPa
|
ISO 527
|
|
Flexural Stress, yield / 彎曲強(qiáng)度,屈服, 2 mm/min
|
85
|
MPa
|
ISO 178
|
|
Flexural Modulus / 撓曲模量, 2 mm/min
|
2200
|
MPa
|
ISO 178
|
|
Hardness / 硬度, H358/30
|
90
|
MPa
|
ISO 2039-1
|
|
IMPACT/沖擊性能
|
Value/值
|
Unit/單位
|
Standard/標(biāo)準(zhǔn)
|
|
Izod Impact, notched / 懸臂梁缺口沖擊強(qiáng)度, 23°C
|
801
|
J/m
|
ASTM D 256
|
|
Izod Impact, notched / 懸臂梁缺口沖擊強(qiáng)度, -30°C
|
678
|
J/m
|
ASTM D 256
|
|
Izod Impact, notched / 懸臂梁缺口沖擊強(qiáng)度, -50°C
|
587
|
J/m
|
ASTM D 256
|
|
Izod Impact, notched / 懸臂梁缺口沖擊強(qiáng)度, 23°C, 6.4mm
|
640
|
J/m
|
ASTM D 256
|
|
Izod Impact, double-gated, 23°C
|
1068
|
J/m
|
SABIC Method
|
|
Instrumented IMPACT Total Energy / 裝有測量儀表的落鏢沖擊總能量, 23°C
|
52
|
J
|
ASTM D 3763
|
|
Izod Impact, unnotched / 無缺口懸臂梁沖擊 80*10*3 +23°C
|
NB
|
kJ/m2
|
ISO 180/1U
|
|
Izod Impact, unnotched / 無缺口懸臂梁沖擊 80*10*3 -30°C
|
NB
|
kJ/m2
|
ISO 180/1U
|
|
Izod Impact, notched / 懸臂梁缺口沖擊強(qiáng)度 80*10*3 +23°C
|
70
|
kJ/m2
|
ISO 180/1A
|
|
Izod Impact, notched / 懸臂梁缺口沖擊強(qiáng)度 80*10*3 -30°C
|
55
|
kJ/m2
|
ISO 180/1A
|
|
Izod Impact, notched / 懸臂梁缺口沖擊強(qiáng)度 63.5*12.7*3.2, 23°C
|
80
|
kJ/m2
|
ISO 180/4A
|
|
Izod Impact, notched / 懸臂梁缺口沖擊強(qiáng)度 63.5*12.7*3.2, -30°C
|
65
|
kJ/m2
|
ISO 180/4A
|
|
Charpy（簡支梁缺口沖擊強(qiáng)度） 23°C, V-notch（V型切口） Edgew 80*10*3 sp=62mm
|
75
|
kJ/m2
|
ISO 179/1eA
|
|
Charpy（簡支梁缺口沖擊強(qiáng)度） -30°C, V-notch（V型切口） Edgew 80*10*3 sp=62mm
|
60
|
kJ/m2
|
ISO 179/1eA
|
|
Charpy（簡支梁缺口沖擊強(qiáng)度） 23°C, Unnotch（無缺口） Edgew 80*10*3 sp=62mm
|
NB
|
kJ/m2
|
ISO 179/1eU
|
|
Charpy（簡支梁缺口沖擊強(qiáng)度） -30°C, Unnotch（無缺口） Edgew 80*10*3 sp=62mm
|
NB
|
kJ/m2
|
ISO 179/1eU
|
|
THERMAL/熱性能
|
Value/值
|
Unit/單位
|
Standard/標(biāo)準(zhǔn)
|
|
Vicat Softening Temp, Rate / 維卡軟化溫度，等級 B/50
|
142
|
°C
|
ASTM D 1525
|
|
HDT（熱變形溫度）, 0.45 MPa, 3.2 mm, unannealed （未退火）
|
134
|
°C
|
ASTM D 648
|
|
HDT（熱變形溫度）, 1.82 MPa, 3.2mm, unannealed （未退火）
|
120
|
°C
|
ASTM D 648
|
|
HDT（熱變形溫度）, 1.82 MPa, 6.4 mm, unannealed （未退火）
|
124
|
°C
|
ASTM D 648
|
|
CTE（線形膨脹系數(shù)）, -40°C to 40°C, flow（流動）
|
6.66E-05
|
1/°C
|
ASTM E 831
|
|
CTE（線形膨脹系數(shù)）, -40°C to 40°C, xflow（橫向）
|
6.66E-05
|
1/°C
|
ASTM E 831
|
|
CTE（線形膨脹系數(shù)）, 23°C to 80°C, flow（流動）
|
7.2E-05
|
1/°C
|
ISO 11359-2
|
|
CTE（線形膨脹系數(shù)）, 23°C to 80°C, xflow（橫向）
|
7.7E-05
|
1/°C
|
ISO 11359-2
|
|
Ball Pressure Test, 125°C +/- 2°C
|
PASSES
|
–
|
IEC 60695-10-2
|
|
Vicat Softening Temp, Rate / 維卡軟化溫度，等級 B/50
|
140
|
°C
|
ISO 306
|
|
Vicat Softening Temp, Rate / 維卡軟化溫度，等級 B/120
|
142
|
°C
|
ISO 306
|
|
HDT（熱變形溫度）/Be, 0.45MPa Edgew 120*10*4 sp=100mm
|
135
|
°C
|
ISO 75/Be
|
|
HDT（熱變形溫度）/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm
|
124
|
°C
|
ISO 75/Ae
|
|
Relative Temp Index, Elec / 相對熱指數(shù)， 電性能
|
125
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/impact / 相對熱指數(shù)，機(jī)械沖擊性能
|
115
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/o impact / 相對熱指數(shù)，非機(jī)械沖擊性能
|
120
|
°C
|
UL 746B
|
|
PHYSICAL/物理性能
|
Value/值
|
Unit/單位
|
Standard/標(biāo)準(zhǔn)
|
|
Specific Gravity / 比重
|
1.18
|
–
|
ASTM D 792
|
|
Mold Shrinkage / 收縮率, flow（流動）, 3.2 mm
|
0.4 – 0.8
|
%
|
SABIC Method
|
|
Mold Shrinkage / 收縮率, xflow（橫向）, 3.2 mm
|
0.4 – 0.8
|
%
|
SABIC Method
|
|
Melt Flow Rate / 熔流率,, 300°C/1.2 kgf
|
10
|
g/10 min
|
ASTM D 1238
|
|
Density / 密度
|
1.19
|
g/cm3
|
ISO 1183
|
|
Water Absorption / 吸水率, (23°C/sat)
|
0.35
|
%
|
ISO 62
|
|
Moisture Absorption / 吸水率, 平衡 (23°C / 50% RH)
|
0.15
|
%
|
ISO 62
|
|
Melt Volume Rate / 溶化體積流率, MVR at 300°C/1.2 kg
|
9
|
cm3/10 min
|
ISO 1133
|
|
ELECTRICAL/電氣性能
|
Value/值
|
Unit/單位
|
Standard/標(biāo)準(zhǔn)
|
|
Dielectric Strength, in oil / 耐電強(qiáng)度，在油中, 3.2 mm
|
17
|
kV/mm
|
ASTM D 149
|
|
Relative Permittivity / 相對介電常數(shù), 50/60 Hz
|
2.95
|
–
|
ASTM D 150
|
|
Relative Permittivity / 相對介電常數(shù), 1 MHz
|
2.9
|
–
|
ASTM D 150
|
|
Dissipation Factor / 耗散因素, 50/60 Hz
|
0.0024
|
–
|
ASTM D 150
|
|
Dissipation Factor / 耗散因素, 1 MHz
|
0.0085
|
–
|
ASTM D 150
|
|
Hot Wire Ignition / 熱絲引燃 {PLC)
|
1
|
PLC Code
|
UL 746A
|
|
High Ampere Arc Ign, surface / 高電流電弧引燃，表面 {PLC}
|
0
|
PLC Code
|
UL 746A
|
|
Comparative Tracking Index / 相比耐漏電起痕指數(shù) (UL) {PLC}
|
3
|
PLC Code
|
UL 746A
|
|
Volume Resistivity / 體積電阻率
|
>1.E+15
|
Ohm-cm
|
IEC 60093
|
|
Surface Resistivity ROA / 表面電阻率
|
>1.E+15
|
Ohm
|
IEC 60093
|
|
Dielectric Strength, in oil / 耐電強(qiáng)度，在油中, 3.2 mm
|
16
|
kV/mm
|
IEC 60243-1
|
|
Relative Permittivity / 相對介電常數(shù), 50/60 Hz
|
2.6
|
–
|
IEC 60250
|
|
Relative Permittivity / 相對介電常數(shù), 1 MHz
|
2.7
|
–
|
IEC 60250
|
|
Dissipation Factor / 耗散因素, 50/60 Hz
|
0.001
|
–
|
IEC 60250
|
|
Dissipation Factor / 耗散因素, 1 MHz
|
0.0085
|
–
|
IEC 60250
|
|
Comparative Tracking Index / 相比耐漏電起痕指數(shù)
|
225
|
V
|
IEC 60112
|
|
FLAME CHARACTERISTICS/火焰特性
|
Value/值
|
Unit/單位
|
Standard/標(biāo)準(zhǔn)
|
|
UL Recognized, 94V-0 Flame Class Rating / 阻燃等級 (3)
|
1.49
|
mm
|
UL 94
|
|
UL Recognized, 94-5VA Rating (3)
|
2.99
|
mm
|
UL 94
|
|
Glow Wire Flammability Index / 灼熱絲易燃指數(shù) 960°C, passes at
|
1
|
mm
|
IEC 60695-2-12
|
|
Glow Wire Ignitability Temperature / 熱燈絲點火溫度, 1.0 mm
|
825
|
°C
|
IEC 60695-2-13
|
|
Oxygen Index / 極限氧指數(shù) (LOI)
|
35
|
%
|
ISO 4589
|
|
UV-light, water exposure/immersion / 紫外線暴露，耐水/浸漬
|
F1
|
–
|
UL 746C
|