| 產(chǎn)品參數(shù) | | 品牌 | Makrolon | | 產(chǎn)品特性 | 防火PC | | 是否進(jìn)口 | 否 | | 產(chǎn)地 | 德國 | | 廠家(產(chǎn)地) | 科思創(chuàng) | | 牌號 | 2665 | | 銷售方式 | 品牌經(jīng)銷 | | 品名 | PC | | 加工級別 | 注塑級 | | 特性級別 | 阻燃級 | | 產(chǎn)品規(guī)格 | 25KG/包 | | 可售賣地 | 全國 | | 類型 | 標(biāo)準(zhǔn)料 | | 科思創(chuàng)（拜耳）防火PC Makrolon 2665 MVR (300°C/1.2 kg) 12 cm3/10 min; flame retardant; UL 94V-2/1.5 mm and 3.0 mm; medium viscosity; easy release; injection molding - melt temperature 280 - 320°C; available in transparent, translucent and opaque colors
Density?(23°C) | 1.20 | g/cm3 | ISO 1183 | Apparent (Bulk) Density?3 | 0.64 | g/cm3 | ISO 60 | Melt Mass-Flow Rate (MFR)?(300°C/1.2 kg) | 13 | g/10 min | ISO 1133 | Melt Volume-Flow Rate (MVR)?(300°C/1.2 kg) | 12 | cm3/10min | ISO 1133 |
Tensile Modulus?(23°C) | 2400 | MPa | ISO 527-2/1 | Tensile Stress |
|
| ISO 527-2/50 | Yield, 23°C | 66.0 | MPa |
| Break, 23°C | 70.0 | MPa |
|
Charpy Notched Impact Strength?7 |
|
| ISO 179/1eA | -30°C, Complete Break | 16 | kJ/m2 |
| 23°C, Partial Break | 70 | kJ/m2 |
|
Heat Deflection Temperature |
|
|
| 0.45 MPa, Unannealed | 136 | °C | ISO 75-2/B | 1.8 MPa, Unannealed | 124 | °C | ISO 75-2/A | Glass Transition Temperature?8 | 144 | °C | ISO 11357-2 |
?PC塑膠原料的吸水率較大，加工 定要預(yù)熱干燥，純PC干燥120℃，改性PC一般用110℃溫度干燥4小時以上。干燥時間不能超過10小時。一般可用對空擠出法判斷干燥是否足夠。再生料的使用比例可達(dá)20。在某些情況下，可 的使用再生料，實際份量要視制品的品質(zhì)要求而定。再生料不能同時混合不同的色母粒，否則會嚴(yán)重?fù)p壞成品的性質(zhì)。