日本三菱耐候易脫模PC Iupilon S-2000VUR Density | 1.20 | g/cm3 | ISO 1183 | Melt Mass-Flow Rate (MFR)?(300°C/1.2 kg) | 10 | g/10 min | ISO 1133 | Melt Volume-Flow Rate (MVR)?(300°C/1.2 kg) | 9.00 | cm3/10min | ISO 1133 | Molding Shrinkage |
|
| Internal Method | Across Flow | 0.50 to 0.70 | |
| Flow | 0.50 to 0.70 | |
| Water Absorption?(Saturation, 23°C) | 0.24 | | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method | Tensile Modulus | 2400 | MPa | ISO 527-2/1 | Tensile Stress?(Yield) | 61.0 | MPa | ISO 527-2/50 | Tensile Strain |
|
| ISO 527-2/50 | Yield | 5.6 | |
| Break | 110 | |
| Flexural Modulus?3 | 2300 | MPa | ISO 178 | Flexural Stress?3 | 93.0 | MPa | ISO 178 | | Impact | Nominal Value | Unit | Test Method | Charpy Notched Impact Strength?(23°C) | 76 | kJ/m2 | ISO 179 | Charpy Unnotched Impact Strength?(23°C) | No Break |
| ISO 179 |
| Thermal | Nominal Value | Unit | Test Method | Heat Deflection Temperature |
|
|
| 0.45 MPa, Unannealed | 143 | °C | ISO 75-2/B | 1.8 MPa, Unannealed | 129 | °C | ISO 75-2/A |
Flame Rating |
|
| UL 94 | 0.38 mm | V-2 |
|
| 1.5 mm | V-2 |
|
| 3.0 mm | V-2 |
|
|
? PC及PC合金可做計(jì)算機(jī)架，外殼及輔機(jī)，打印機(jī)零件。改性PC耐高能輻射殺菌，耐蒸煮和烘烤消毒，可用于采血標(biāo)本器具，血液充氧器，外科手術(shù)器械，腎透析器等，PC可做頭盔和安全帽，防護(hù)面罩，墨鏡和運(yùn)動(dòng)護(hù)眼罩。 PC薄膜 用于印刷圖表，醫(yī)藥包裝，膜式換向器 
|