HOPELEN J-150H
聚丙烯均聚物
Lotte Chemical Corporation
產(chǎn)品說(shuō)明:
J-150H is homo polymer resin produced through the polymerization of propylene. This grade is designed to be processed in conventional injection molding equipment and offers high flow, high stiffness, heat stability, scratch resistance and high surface gloss.
產(chǎn)品說(shuō)明 | |
J-150H is homo polymer resin produced through the polymerization of propylene. This grade is designed to be processed in conventional injection molding equipment and offers high flow, high stiffness, heat stability, scratch resistance and high surface gloss. | |
總體 | |
材料狀態(tài) | · 已商用：當(dāng)前有效 |
資料 1 | · Technical Datasheet (English) |
搜索 UL 黃卡 | · Lotte Chemical Corporation |
供貨地區(qū) | · 北美洲· 歐洲· 亞太地區(qū)
|
特性 | · 剛性，高· 高光· 均聚物· 流動(dòng)性高· 耐刮擦性· 熱穩(wěn)定性，良好
|
用途 | · 電氣/電子應(yīng)用領(lǐng)域· 電器用具· 玩具
|
加工方法 | · 注射成型 |
物理性能 | 額定值 | 單位制 | 測(cè)試方法 |
比重 | 0.900 | g/cm3 | ASTM D792, ISO 1183 |
熔流率（熔體流動(dòng)速率） (230°C/2.16 kg) | 12 | g/10 min | ASTM D1238, ISO 1133 |
機(jī)械性能 | 額定值 | 單位制 | 測(cè)試方法 |
抗張強(qiáng)度 | |||
屈服 | 34.3 | MPa | ASTM D638 |
屈服 | 32.4 | MPa | ISO 527-2 |
伸長(zhǎng)率 (斷裂) | > 100 | % | ASTM D638, ISO 527-2 |
彎曲模量 | |||
-- | 1620 | MPa | ASTM D790 |
-- | 1270 | MPa | ISO 178 |
沖擊性能 | 額定值 | 單位制 | 測(cè)試方法 |
懸壁梁缺口沖擊強(qiáng)度 | |||
-10°C | 25 | J/m | ASTM D256 |
-10°C | 20 | J/m | ISO 180 |
23°C | 29 | J/m | ASTM D256 |
23°C | 25 | J/m | ISO 180 |
熱性能 | 額定值 | 單位制 | 測(cè)試方法 |
載荷下熱變形溫度 | |||
0.45 MPa, 未退火 | 115 | °C | ASTM D648 |
0.45 MPa, 未退火 | 95.0 | °C | ISO 75-2/B |