NORYL Resin GFN3濾材用環(huán)保PPO
特點(diǎn)：PPE+PS，NSF61，尺寸穩(wěn)定性好,水解穩(wěn)定,工程應(yīng)用。PPE + PS混合。30%的玻璃纖維。NSF61。FDA合規(guī)(限制)。低吸水率。水解穩(wěn)定性。尺寸穩(wěn)定性。
物性：溶指8.7，收縮率0.1-0.4%，吸水率0.06%，洛氏硬度計(jì)108L，沖擊強(qiáng)度120J/M，熱變形溫度137-158℃，維卡軟化溫度143-147℃，加工熔體溫度299-327℃。
| TYPICAL PROPERTIES (1) | ||||
| MECHANICAL | Value | Unit | Standard | |
| Tensile Stress, brk, Type I, 5 mm/min | 1180 | kgf/cm2 | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 2 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 93300 | kgf/cm2 | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 1830 | kgf/cm2 | ASTM D 790 | |
| Flexural Stress, yld, 2.6 mm/min, 100 mm span | 1650 | kgf/cm2 | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 81500 | kgf/cm2 | ASTM D 790 | |
| Flexural Modulus, 2.6 mm/min, 100 mm span | 73100 | kgf/cm2 | ASTM D 790 | |
| Hardness, Rockwell L | 108 | - | ASTM D 785 | |
| Tensile Stress, break | 117 | MPa | ISO 527 | |
| Tensile Strain, break | 1.8 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 8740 | MPa | ISO 527 | |
| Flexural Stress | 183 | MPa | ISO 178 | |
| Flexural Modulus | 8710 | MPa | ISO 178 | |
| IMPACT | Value | Unit | Standard | |
| Izod Impact, unnotched, 23°C | 59 | cm-kgf/cm | ASTM D 4812 | |
| Izod Impact, notched, 23°C | 11 | cm-kgf/cm | ASTM D 256 | |
| Izod Impact, notched, -30°C | 12 | cm-kgf/cm | ASTM D 256 | |
| Izod Impact, unnotched 80*10*4 +23°C | 31 | kJ/m2 | ISO 180/1U | |
| Izod Impact, unnotched 80*10*4 -30°C | 35 | kJ/m2 | ISO 180/1U | |
| Izod Impact, notched 80*10*4 +23°C | 12 | kJ/m2 | ISO 180/1A | |
| Izod Impact, notched 80*10*4 -30°C | 11 | kJ/m2 | ISO 180/1A | |
| Charpy Impact, notched, 23°C | 12 | kJ/m2 | ISO 179/2C | |
| Charpy Impact, notched, -30°C | 11 | kJ/m2 | ISO 179/2C | |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 39 | kJ/m2 | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 47 | kJ/m2 | ISO 179/1eU | |
| THERMAL | Value | Unit | Standard | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 142 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 137 | °C | ASTM D 648 | |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 158 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 137 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 3.06E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 6.18E-05 | 1/°C | ASTM E 831 | |
| Vicat Softening Temp, Rate B/50 | 143 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 147 | °C | ISO 306 | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 143 | °C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 137 | °C | ISO 75/Af | |
| Relative Temp Index, Elec | 90 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 90 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 90 | °C | UL 746B | |
| PHYSICAL | Value | Unit | Standard | |
| Specific Gravity | 1.29 | - | ASTM D 792 | |
| Water Absorption, 24 hours | 0.06 | % | ASTM D 570 | |
| Mold Shrinkage, flow, 3.2 mm (5) | 0.1 - 0.4 | % | SABIC Method | |
| Melt Flow Rate, 300°C/5.0 kgf | 8.6 | g/10 min | ASTM D 1238 | |
| Melt Volume Rate, MVR at 300°C/5.0 kg | 7 | cm3/10 min | ISO 1133 | |
| ELECTRICAL | Value | Unit | Standard | |
| Dielectric Strength, in oil, 3.2 mm | 21.6 | kV/mm | ASTM D 149 | |
| Relative Permittivity, 50/60 Hz | 2.93 | - | ASTM D 150 | |
| Dissipation Factor, 50/60 Hz | 0.0009 | - | ASTM D 150 | |
| Arc Resistance, Tungsten {PLC} | 7 | PLC Code | ASTM D 495 | |
| Hot Wire Ignition {PLC) | 4 | PLC Code | UL 746A | |
| High Voltage Arc Track Rate {PLC} | 3 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 4 | PLC Code | UL 746A | |
| Comparative Tracking Index (UL) {PLC} | 4 | PLC Code | UL 746A | |
| FLAME CHARACTERISTICS | Value | Unit | Standard | |
| UL Recognized, 94HB Flame Class Rating (3) | 1.47 | mm | UL 94 | |
| Oxygen Index (LOI) | 26 | % | ASTM D 2863 | |