ULTEM 2312EPR高流動磨碎玻璃填充PEI
SABIC Innovative Plastics ULTEM 2312EPR PEI
PEI 基礎(chǔ)創(chuàng)新塑料（美國）2312EPR
ULTEM Resin 2312EPR
聚醚酰亞胺ULTEM 2312EPR，30%磨碎的玻璃,高流量Polyetherimide(Tg 217 c)與內(nèi)部脫模和增強electroplatability。符合ECO。阻燃UL94 V0和5VA。
物理性能：
| Specific Gravity | 1.48 g/cc | 1.48 g/cc | ASTM D792 |
| Density | 1.48 g/cc | 0.0535 lb/in3 | ISO 1183 |
| Moisture Absorption | 0.500 % | 0.500 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.90 % | 0.90 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | on Tensile Bar; SABIC Method |
|
0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse |
0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow |
13.7 g/10 min @Load 6.60 kg, Temperature 337 °C |
13.7 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
| Melt Index of Compound |
14 g/10 min @Load 5.00 kg, Temperature 360 °C |