超強(qiáng)沖擊強(qiáng)度PA6 Durethan BKV 130 000000
PA6 德國(guó)朗盛 BKV130
Lanxess Durethan BKV 130 000000 Copolyamide, 30% Glass Fiber
性能特點(diǎn)：復(fù)合PA(共聚酰胺）注塑級(jí),30%玻璃纖維,添加脫模劑，彈性體改性,可電鍍,在干燥狀態(tài)下較BKV30在雙軸沖擊荷載作用下，具有更高的切口沖擊強(qiáng)度和更高的能量吸收。
應(yīng)用實(shí)例:雪橇的折疊機(jī)制。
物理性能：
| Density | 1.36 g/cc | 0.0491 lb/in3 | ISO 1183 |
| Water Absorption | 7.0 % | 7.0 % | Test Sim. to ISO 62 |
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | 23°C/50% R.H.; Test Sim. to ISO 62 |
| Viscosity Test | 134 cm3/g | 134 cm3/g | Viscosity number; ISO 307, 1157, 1628 |
| Melt Flow |
13 g/10 min @Load 5.00 kg, Temperature 260 °C |
13 g/10 min @Load 11.0 lb, Temperature 500 °F |
Calculated from MVR using melt density; ISO 1133 |
機(jī)械性能：
| Tensile Strength at Break | 100 MPa | 14500 psi | Conditioned; ISO 527-1/-2 |
| 160 MPa | 23200 psi | ISO 527-1/-2 | |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527-1/-2 |
| 7.0 % | 7.0 % | Conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 5.20 GPa | 754 ksi | Conditioned; ISO 527-1/-2 |
| 9.00 GPa | 1310 ksi | ISO 527-1/-2 | |
Charpy Impact Unnotched 
|
8.00 J/cm2 @Temperature -30.0 °C |
38.1 ft-lb/in2 @Temperature -22.0 °F |
ISO 179/1eU |
|
8.00 J/cm2 @Temperature -30.0 °C |
38.1 ft-lb/in2 @Temperature -22.0 °F |
Conditioned; ISO 179/1eU | |
|
9.50 J/cm2 @Temperature 23.0 °C |
45.2 ft-lb/in2 @Temperature 73.4 °F |
ISO 179/1eU | |
|
11.0 J/cm2 @Temperature 23.0 °C |
52.3 ft-lb/in2 @Temperature 73.4 °F |
Conditioned; ISO 179/1eU | |
|
Charpy Impact, Notched
|
1.00 J/cm2 @Temperature -30.0 °C |
4.76 ft-lb/in2 @Temperature -22.0 °F |
ISO 179/1eA |
|
1.00 J/cm2 @Temperature -30.0 °C |
4.76 ft-lb/in2 @Temperature -22.0 °F |
Conditioned; ISO 179/1eA | |
|
1.80 J/cm2 @Temperature 23.0 °C |
8.57 ft-lb/in2 @Temperature 73.4 °F |
ISO 179/1eA | |
|
2.80 J/cm2 @Temperature 23.0 °C |
13.3 ft-lb/in2 @Temperature 73.4 °F |
Conditioned; ISO 179/1eA | |
| Impact | 1024 | 1024 | Puncture maximum force (N); ISO 6603-2 |
|
|
835 @Temperature -30.0 °C |
835 @Temperature -22.0 °F |
Puncture maximum force (N); ISO 6603-2 |
| Puncture Energy | 10.0 J | 7.38 ft-lb | ISO 6603-2 |
| 15.0 J | 11.1 ft-lb | Conditioned; ISO 6603-2 | |
|
|
7.00 J @Temperature -30.0 °C |
5.16 ft-lb @Temperature -22.0 °F |
ISO 6603-2 |
|
7.00 J @Temperature -30.0 °C |
5.16 ft-lb @Temperature -22.0 °F |
Conditioned; ISO 6603-2 | |
| Tensile Creep Modulus, 1 hour | 4200 MPa | 609000 psi | ISO 899-1 |
| Tensile Creep Modulus, 1000 hours | 3300 MPa | 479000 psi | ISO 899-1 |