低翹曲電鍍級尼龍6 Minlon 73M30
PA6 美國杜邦 73M30 NC010
DuPont Performance Polymers Minlon 73M30 NC010 Nylon 6Minlon 73m30 NC010是30%的礦物增強(qiáng)，熱穩(wěn)定聚酰胺6樹脂注塑成型。它具有各向同性性能和低翹曲。添加脫模劑，特性：熱穩(wěn)定性或耐熱性能，可電鍍。
物性：
| Density | 1.35 g/cc | 0.0488 lb/in3 | DAM; ISO 1183 |
| Water Absorption |
6.3 % @Thickness 2.00 mm |
6.3 % @Thickness 0.0787 in |
DAM; Sim. to ISO 62 |
| Moisture Absorption |
2.10 % @Thickness 2.00 mm |
2.10 % @Thickness 0.0787 in |
DAM; Sim. to ISO 62 |
| Viscosity Test | 145 cm3/g | 145 cm3/g | DAM; ISO 307 1157 1628 |
| Linear Mold Shrinkage, Flow | 0.0090 cm/cm | 0.0090 in/in | DAM; ISO 294-4 2577 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | DAM; ISO 294-4 2577 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 88.0 μm/m-°C | 48.9 μin/in-°F | DAM; ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 102 μm/m-°C | 56.7 μin/in-°F | DAM; ISO 11359-1/-2 |
| Melting Point | 221 °C | 430 °F | DAM; 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 196 °C | 385 °F | DAM; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 78.0 °C | 172 °F | DAM; ISO 75-1/-2 |
| Vicat Softening Point | 210 °C | 410 °F | DAM; 50°C/h 50N; ISO 306 |
| Flammability, UL94 |
HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
DAM; IEC 60695-11-10 |